1. ORCER
RF-60A
RoHS and WEEE Compliant
Exceptional Interlaminar Bonds
Low Moisture Absorption
Enhanced Dimensional Stability
Low Z-Axis Expansion
Stable Dk Over Frequency
Increased Flexural Strength
An ISO 9001:2000 Registered Company
Petersburgh, NY: Tel: 800-833-1805 Fax: 518-658-3988
Europe: Tel: +353-44-9395600 Fax: +353-44-9344369 Asia: Tel: +82-31-704-1858 Fax: +82-31-704-1857
www.taconic-add.com
2. APPLICATIONS
Power Amplifiers
Filters and Couplers
Passive Components
Antennas
RF-60A
RF-60A is an organic-ceramic laminate in the ORCER
family of Taconic products. It is based on woven glass
reinforcement. RF-60A is a result of Taconic’s expertise in both ceramic fill technology and in coated PTFE
fiberglass.
RF-60A exhibits exceptional interlaminar bond
strength and solder resistance. RF-60A’s proprietary
composition results in low moisture absorption and
uniform electrical properties.
RF-60A’s woven glass reinforcement ensures excellent dimensional stability and enhances flexural
strength. The RF-60A laminate exhibits low Z-axis
expansion allowing for plated-through-hole reliability
in extreme thermal environments.
RF-60A laminates are in complete compliance with
RoHS and WEEE directives and are compatible with
the temperatures required for the new lead free solders.
RF-60A laminates can be sheared, drilled, milled and
plated using standard methods for PTFE-woven fiberglass materials.
RF-60A laminates are generally ordered clad on both
sides. Various panel sizes are available. Contact our
customer service department for more information.
RF-60A laminates meet the requirements of IPC-4103
and are tested in accordance with IPC-TM 650. A certificate of compliance containing lot-specific test data
accompanies each shipment.
See “How To Order” on back page for a complete
product listing.
3. RF-60A Typical Values
Property
Dielectric Constant
Dissipation Factor @ 10 GHz
Moisture Absorption
Dielectric Breakdown
Dielectric Strength
Volume Resistivity
Surface Resistivity
Arc Resistance
Flexural Strength (MD)
Flexural Strength (CD)
Tensile Strength (MD)
Tensile Strength (CD)
Youngʼs Modulus
Poissonʼs Ratio
Compressive Modulus
Peel Strength (1 oz ED)
Dimensional Stability (MD)
Dimensional Stability (CD)
Density (Specific Gravity)
Thermal Conductivity
CTE (x)
CTE (y)
CTE (z)
Outgassing (% TML)
Outgassing (% CVCM)
Outgassing (% WVR)
Flammability Rating
Test Method
IPC-TM-650 2.5.5.6
IPC-TM-650 2.5.5.5.1
IPC-TM-650 2.6.2.1
IPC-TM-650 2.5.6
ASTM D 149
IPC-TM-650 2.5.17.1 (Humidity Conditioning)
IPC-TM-650 2.5.17.1 (Humidity Conditioning)
IPC-TM-650 2.5.1
ASTM D 790
ASTM D 790
ASTM D 3039
ASTM D 3039
ASTM D 3039
ASTM D 3039
ASTM D 695 (23ºC)
IPC-TM-650 2.4.8 Sec. 5.2.2 (Thermal Stress)
IPC-TM-650 2.4.39 Sec. 5.4 (After Bake)
IPC-TM-650 2.4.39 Sec. 5.4 (After Bake)
ASTM F 433
ASTM D 3386 (-30ºC - 125ºC)
ASTM D 3386 (-30ºC - 125ºC)
ASTM D 3386 (-30ºC - 125ºC)
ASTM E 595*
ASTM E 595*
ASTM E 595*
UL 94
Unit
Value
6.15
0.0038
%
0.02
kV
53
V/mil
880
Mohm/cm
9.0 x 108
Mohm
2.28 x 108
Seconds
193
kpsi
18.3
kpsi
14.6
kpsi
19.5
kpsi
16.3
kpsi
1590
0.068
kpsi
338
lbs/linear inch
8
mils/in
0.68
mils/in
1.05
3
g/cm
2.79
W/m/K
0.40
ppm/ºC
9
ppm/ºC
8
ppm/ºC
69
%
0.02
%
0.00
%
0.01
V-0
Unit
%
kV
V/mm
Mohm/cm
Mohm
Seconds
N/mm2
N/mm2
N/mm2
N/mm2
N/mm2
N/mm2
N/mm
mm/M
mm/M
g/cm3
W/m/K
ppm/ºC
ppm/ºC
ppm/ºC
%
%
%
Value
6.15
0.0038
0.02
53
34,600
9.0 x 108
2.28 x 108
193
126
101
134
112
11,000
0.068
2,330
1.4
0.68
1.05
2.79
0.40
9
8
69
0.02
0.00
0.01
V-0
*As reported by NASA. See http://outgassing.nasa.gov/og_disclaimer.html.
All reported values are typical and should not be used for specification purposes. In all instances, the user shall determine suitability in any given
application.
4. How To Order
Dielectric
Constant
Designation
RF-60A
Typical
Thicknesses1
0.0100”
0.0250”
0.0310”
0.0500”
0.0600”
0.1250”
6.15 +/- 0.25
Available Sheet Sizes2
0.25 mm
0.64 mm
0.79 mm
1.27 mm
1.52 mm
3.18 mm
12” x 18”
304 mm x 457 mm
16” x 18”
406 mm x 457 mm
18” x 24”
457 mm x 610 mm
Other thicknesses may be available. Please call for information.
Our standard sheet size is 18” x 24” (457 mm x 610 mm). Please contact our customer service department for availability of other sizes.
1
2
Available Copper Cladding
Designation
Weight
RH
R1
CVH (CH)
CV1 (C1)
C2
1/2 oz / ft2
1 oz / ft2
1/2 oz / ft2
1 oz / ft2
2 oz / ft2
Copper
Thickness
~0.0007”
~0.0014”
~0.0007”
~0.0014”
~0.0028”
~18 µm
~35 µm
~18 µm
~35 µm
~70 µm
RMS
Treated Side
16 µin
11 µin
27 µin
25 µin
77 µin
0.4 µm
0.3 µm
0.7 µm
0.6 µm
2.0 µm
Description
Rolled annealed
Rolled annealed
Very low profile / Electrodeposited
Very low profile / Electrodeposited
Electrodeposited
Heavy metal claddings (aluminum, brass & copper) may also be available upon request. Please call for information.
An example of our part number is: RF-60A-0600-CV1/CV1 - 18” x 24” (457 mm x 610 mm)
An ISO 9001:2000 Registered Company
Petersburgh, NY: Tel: 800-833-1805 Fax: 518-658-3988
Europe: Tel: +353-44-9395600 Fax: +353-44-9344369 Asia: Tel: +82-31-704-1858 Fax: +82-31-704-1857
www.taconic-add.com
8/07:100-19