β’ Said to have formed due to a supernova nucleosynthesis.
β’ Its heavy - 19 x water
2 x lead
if we had enough gold to fill a one litre milk carton, it would weigh 19.3 Kg
β’ Gold is quite soft β slightly harder than finger nails
β’ Very malleable and ductile.
β’ Melting point β 1060 c
β’ Boiling point β 2660 c
β’ Atomic mass β 196.97
4. Aurum β β glowing dawn β.
Automic number 79
Automic mass 196.97
Tensile strength 120 MPa
Youngs modulous 79 GPa
5. Why gold ?
β’ Esthetic beauty β high luster.
β’ High malleability and ductility.
β’ Soft
β’ Rare and high appreciation value.
15. β’ Comminution is the breaking up of ore to make gold available for
treatment. Conventionally, this process occurs in multi-stage crushing and
milling circuits. Modern technology is based on large mills fed directly with
run-of-mine material.
β’ Gold ores can typically be classified into:
β’ refractory ores, where the gold is locked within a sulphide mineral and not
readily available for recovery by the cyanidation process; or
β’ free milling, where the gold is readily available for recovery by the
cyanidation process.
β’ Refractory ore treatment β after fine grinding, the sulphide materials are
floated away from the barren gangue material to produce a high-grade
sulphide concentrate. The sulphide concentrate is oxidised by either
roasting as at AngloGold Ashanti Mineração or bacterial oxidation (BIOX)
as at Obuasi. The oxidation process oxidises the sulphide minerals
liberating the gold particles making them amenable to recovery by the
cyanidation process.
17. Making gold jewelry
β’ Making gold jewelry takes time and craftsmanship. Weather you are making 14k
custom gold jewelry or 24k gold jewelry, the process is the same. You start with
your design and from there a wax model is carved . Many tools and techniques are
used to create a wax: steel wax carvers, files, hand gravers, burs, drills, heat, etc. -
whatever is required to achieve a finished model. Then the wax is ready for
investing. β¨β¨The next step in making gold jewelry is to invest. We first attach a
sprue to the wax. The sprue will serve as a channel for melting wax to escape
during burn-out and later for molten gold to enter during casting. β¨β¨Then the
sprued wax is attached to a round rubber base. An investment flask is placed over
the wax and is attached to the rubber base. The investment flask is a round
cylindrical steel tube, similar to a tin can open at both ends.
β’ Investment begins as a dry fine white powder similar to plaster-of-paris in feel. It is
18. β’ This is done by placing the investment slurry in a vacuum where the air is drawn
out. This is called debubblizing. The slurry is then poured into the flask completely
surrounding the wax. The flask is then placed into the vacuum chamber for a final
debubblizing to make sure there are no air pockets attached to the model that
would corrupt the casting. β¨β¨After the investment hardens the rubber base is
removed and the flask goes into the burn-out oven. The burn-out takes hours at a
high temperature until all the wax is eliminated. Once the burn-out has taken
place only a hollow replica of the original wax carving remains inside the flask.
β¨β¨The mold is ready for casting. The flask is placed in a casting machine and the
gold is melted in a crucible with a torch. At the proper casting temperature the
molten gold is thrown by centrifugal force into the hollow mold and held there
until it solidifies. Now you have a cast replica of your βlostβ wax. β¨β¨The investment
is then broken away from the cast piece. What remains is the rough casting. Now
itβs time to clean up and polish the casting. The gold jewelry making process is
complete! β¨
22. The price of gold fluctuates according to the
demand of the buyers and the amount being
sold by the sellers.
The term carat in 24K gold refers to the amount
of base metals mixed in the alloy.. 24K being the
purest form.