The document discusses polyvinyl chloride (PVC) paste polymerization and plastisols. It describes suspension, emulsion, and microsuspension polymerization methods. Plastisol applications include leather cloth, textiles, coatings, and more. India's PVC paste resin demand and imports are growing about 7% annually. Primary PVC particles from emulsion polymerization are 0.1-2 micrometers and form porous secondary particles after spray drying. Plastisol rheology depends on particle size distribution and residual emulsifiers. Upon heating, plasticizers diffuse into PVC particles to form a homogeneous material, with complete fusion providing maximum properties.
3. Polymerization - Introduction
Polymer: Large chain molecules having high molecular weight
- made up of monomers
Polymerization
m number of
single chains
PVC Particle
Free radical: Highly reactive molecule having an unpaired valency electron
4. Fikentscher K-Value: Measure of mean molecular weight, derived from
relative viscosity of polymer solutions
Polymerization - Introduction
5. Suspension polymerisation:
• Monomer soluble free radical initiator
• Dispersion droplet size is large, giving polymer particles of a size greater than about 50 µm
• Particles can be separated by centrifuging or filtering
• Suspending agents - cellulose ethers, polyvinyl alcohol – not true surfactants
• Stirring is required
Emulsion polymerisation:
• Water soluble initiators
• Latex of particles usually of less than 1 µm
• Particles cannot be separated from the aqueous phase by centrifuging or filtering
• Droplet dispersion is normally stable on standing
Microsuspension polymerisations:
• Monomer soluble initiator
• Homogeniser is used to form a dispersion
• Latex particles usually less than 2 µm (sometimes up to 20 µm)
• Needs special separation technique - Spray drying
Polymerization - Introduction
Suspension Polymer Emulsion Polymer Micro-suspension Polymer
7. 2010-11 2011-12 2012-13 2013-14 2014-15 2015-16
Total Demand(Kt) 79 84 103 109 126 134
Domestic Supply (Kt) 44 55 56 69 78 84
Imports (Kt) 35 29 47 40 48 50
Total Demand Growth (%) 14% 6% 23% 5% 15% 7%
0%
5%
10%
15%
20%
25%
0
20
40
60
80
100
120
140
160
Growth(%)
Quantity(Kt)
Year
Paste resin – Supply and Demand
Germany
10%
Korea
44%
Taiwan
18%
U S A
11%
Japan
7%
Others
10%
Avg. Imports - 2015
Germany Korea Taiwan U S A Japan Others
8. Plastisol: Dispersion of PVC in plasticizer
Rheology: Study of deformation and flow of material
Viscosity-η: Resistance to flow
Shear stress-τ: Force per unit surface area
Shear rate-D: Ratio between the speed difference of two adjacent
layers of a liquid and their distance apart
Rheology - overview
10. Pseudoplasticity: Viscosity-η decreases as Shear rate-D increases
Ketchup can have its viscosity reduced by shaking
Toothpaste is a Plastic
Rheology - overview
11. Dilatancy: Viscosity-η increases as Shear rate-D increases
Cornstarch - Common thickening agent used in cooking
When a force is applied to a 1:2.5 mixture of water and cornstarch,
It acts as a solid and resists the force
Dilatant materials used as a liquid body armor
Thixotropy: Viscosity falls following a prolonged mechanical effort
Rheopexy: Viscosity increases after a prolonged mechanical effort
These effects are reversible
Rheology - overview
Plastisol Selection & Rheology:
Fabric Coating
Coating penetration is deeper low yield value plastisols (Low Viscosity)
Coating penetration is shallower Pseudoplastic plastisols (High Initial Viscosity)
High Coating Speed High shear rate fluid plastisols (Pseudoplastic)
Low Coating Speed(< 15 m/min) Low to medium shear rate fluid plastisols (Dilatant)
12. Emulsion: Stabilized mixture (dispersion) of two or more immiscible liquids,
like oil and water E.g. Milk
Emulsifier: Binds molecules of immiscible liquids and mixes them to form a
homogenous solution
Emulsion - Introduction
Critical Micellar Concentration (CMC): Threshold concentration above which surfactant
molecules undergo self-association
Addition of further surfactant above the CMC all goes toward
increasing the number of micelles
Macroscopically homogeneous but microscopically heterogeneous
CMC & Aggregation number decide the number of micelles formed at the start of
polymerisation and hence the ultimate particle size
With
Co surfactant
13. Lowers the interfacial tension to a small value which facilitates dispersion process
Has control on emulsion viscosity and droplet size
Forms thermodynamically stable dispersion
Provides sufficient flexibility to the interfacial film that can readily deform
around the droplets
Reduces energy input since high speed agitation is not necessary
Blended Alcohol – As a Cosurfactant
14. Secondary Particles - ø: 20 to 60 µm - After Spray Drying
Primary Particles - ø : 0.1 to 2.0 µm - After Polymerisation
Final Resin - ø : 2.0 to 60.0 µm - After Grinding
Secondary particles: Porous and contain internal cavities caused by the rapid evaporation of
water enclosed in the particles during formation (Spray Drying)
MSP Primary Particles: Having Mono-modal PSD that prevents efficient packing of particles
during Spray drying process Produce 2º Particles with high porosity
SEM Images of Resin Particles
15. Continuous gradation of sizes Small particles
Fit into the interstices of the larger particles (efficient packing)
Releases plasticiser from the interstices between the larger particles
Comparatively low viscosity plastisol
MSP 1º Particles (Broad uni-modal distribution) low shear viscosity at low shear rates
Higher shear rates Breaks efficient packing Dilatancy
Packing of Resin Particles
16. • Partial homogenization or homogenization with different pressures & Emulsifier
Broad PSD
• Proper Emulsifier Type & Quantity Good Droplet stability
Spherical particles & No Surface damages
• Residual Emulsifier (Before drying) Reduces resin Tg / act as Cementing agent
Forms highly cohesive 2º Particles from spray drying
Reduces de-agglomeration rate Reduces viscosity aging and its rate
• Residual Emulsifier Interact with polymer / plasticiser interface
Inter-particles repulsion high viscosities at low shear rates
Towards - pseudoplasticity
S.NO Emulsifier Primary particle size
1 SLS 1 – 3 μ
2 AOS 2 – 5 μ
3 Calsolene Oil 18 – 20 μ
4 Na Dioctyl Sulfo Succinamide 0.2 – 1 μ
5 Ethoxylated Fatty Alcohol 0.2 – 1 μ
Residual Emulsifiers:
•Reduce gloss and clarity
•Not facilitate air release
•Poor heat stability
•Fog formation
•Affect taste/ acceptability in food packing
•Poor compatibility with thermal stabilizer
•Accelerate plateout
• Increasing slurry viscosity Narrow spray angle larger droplets coarser 1º particles
Reduces the available surface area for plasticiser absorption
Increases free plasticiser Depresses shear viscosity
• Increasing atomizer speed Smaller droplets highly fused porous 2º Particles
Absorption and Immobilization of some plasticiser Swelling
Increases initial viscosity, Reduces viscosity aging and its rate
• Grinding Fragments of secondary particles Rapid de-agglomeration (with Plasticiser)
Enhances plastisol forming process
• Grinding - very high cohesive 2º Particles Irregularly shaped fragments
Surface retention of plasticiser, Internal 1º particles swelling
Decreases free plasticiser level Increases low shear viscosity
17. PVC / DOP – at 90ºC
PVC / DOP – at 160ºC
PVC / DOP – at 130ºC
PVC / DOP – at 193ºC
Surfactant layer prevents plasticizer adsorption at room temperature
Heating diffuses plasticizer into PVC particles and fuses into a homogeneous material at
higher temperatures
Complete Fusion: Clarity, gloss and mechanical strength of the final composition reaches
the maximum
Stages of Plastisol Fusion
Blowing agent decomposes before fusion Open Cell
Decomposition happens after plastisol-fusion Closed Cell
Cell Size ∞ Decomposition rate of BA & Melt viscosity of the fused plastisol