![Test Report Report No.: AJFS2209007225FF Date: SEP.19, 2022 Page 2 of 3
I. Test Conducted
The test was conducted in accordance with ISO 6925:1982 Textile floor covering-Burning behavior - Tablet
test at ambient temperature.
II. Sample details
Sample Description Sample A: Fabric; Sample B: Fabric
Color Sample A: Dark grey; Sample B: Black
Using an underlay [ ] Yes; [ √ ] No
Specimen size 230 mm × 230 mm
Conditioning:
Sample A: Prior to testing, place the specimens in the oven at 105 ± 2°C for 2 h, and then move the
specimens into the desiccator for at least 1 h, until they reach the ambient temperature.
Sample B: Prior to testing, the specimens were conditioned for at least 24 h at a temperature of 20±2°C and a
relative humidity of 65±2%.
III. Test results
Sample A
Specimen No. 1 2 3 4 5 6 7 8
The maximum distance between the centre
of the specimen and the edge of the
damaged zone (mm)
24 27 18 20 17 22 21 24
The time from the ignition of the tablet to the
moment when the flame or glowing reaches
the edge of the hole in the metal plate (s)
0 0 0 0 0 0 0 0
Sample B
Specimen No. 1 2 3 4 5 6 7 8
The maximum distance between the centre
of the specimen and the edge of the
damaged zone (mm)
17 22 19 25 18 20 22 25
The time from the ignition of the tablet to the
moment when the flame or glowing reaches
the edge of the hole in the metal plate (s)
0 0 0 0 0 0 0 0](data:image/gif;base64,R0lGODlhAQABAIAAAAAAAP///yH5BAEAAAAALAAAAAABAAEAAAIBRAA7)
Recomendados
Recomendados
Más contenido relacionado
Similar a 阻燃测试AJFS2209007225FF (1).pdf
Similar a 阻燃测试AJFS2209007225FF (1).pdf (20)
Más de Feng Freddy
Más de Feng Freddy (16)
Último
Último (20)
阻燃测试AJFS2209007225FF (1).pdf
- 1. Allen Zou Approved Signatory Test Report Report No.: AJFS2209007225FF Date: SEP.19, 2022 Page 1 of 3 Sample Description: 300D OXFORD, 600D OXFORDSGS Ref No.: SHHL2209038474SD Style/Item No.: / Manufacturer: YONGKANG JINLE OUTDOOR SUPPLIES CO., LTD The above sample(s) was / were submitted and identified on behalf of the client. SGS is not responsible for the authenticity, integrity and results of the data and information and / or the validity of the conclusion arising therefrom. Results apply to the sample as received. ****************** Test Requested: ISO 6925:1982 Textile floor covering-Burning behavior - Tablet test at ambient temperature. Test Results: -- See attached sheet -- Test Period: Sample Receiving Date : SEP.13, 2022 Test Performing Date : SEP.13, 2022 TO SEP.17, 2022 Signed for and on behalf of SGS-CSTC Standards Technical Services Co., Ltd. Anji Branch
- 2. Test Report Report No.: AJFS2209007225FF Date: SEP.19, 2022 Page 2 of 3 I. Test Conducted The test was conducted in accordance with ISO 6925:1982 Textile floor covering-Burning behavior - Tablet test at ambient temperature. II. Sample details Sample Description Sample A: Fabric; Sample B: Fabric Color Sample A: Dark grey; Sample B: Black Using an underlay [ ] Yes; [ √ ] No Specimen size 230 mm × 230 mm Conditioning: Sample A: Prior to testing, place the specimens in the oven at 105 ± 2°C for 2 h, and then move the specimens into the desiccator for at least 1 h, until they reach the ambient temperature. Sample B: Prior to testing, the specimens were conditioned for at least 24 h at a temperature of 20±2°C and a relative humidity of 65±2%. III. Test results Sample A Specimen No. 1 2 3 4 5 6 7 8 The maximum distance between the centre of the specimen and the edge of the damaged zone (mm) 24 27 18 20 17 22 21 24 The time from the ignition of the tablet to the moment when the flame or glowing reaches the edge of the hole in the metal plate (s) 0 0 0 0 0 0 0 0 Sample B Specimen No. 1 2 3 4 5 6 7 8 The maximum distance between the centre of the specimen and the edge of the damaged zone (mm) 17 22 19 25 18 20 22 25 The time from the ignition of the tablet to the moment when the flame or glowing reaches the edge of the hole in the metal plate (s) 0 0 0 0 0 0 0 0
- 3. Test Report Report No.: AJFS2209007225FF Date: SEP.19, 2022 Page 3 of 3 Photo Appendix: Sample A Sample B SGS authenticate the photo on original report only ***End of Report***