RDSiR silicone rubber recycling chemical
1. 11
RDS Non-sulfur vulcanized Rubber Reviving Agent
RDS-EPDM EPDM Reviving Agent
RDS-CR CR Reviving Agent
RDS-NBR NBR Reviving Agent
RDS-CPE CPE Reviving Agent
Appearance: light yellow powder
Application:RDS-EPDM、RDS-CR、RDS-NBR、RDS-CPE is respectively applicable to the revivingof EPDM, CR, NBR, CPE
and non-sulfur vulcanized rubber.
Application Recipe:
Waste rubber
RDS
Total
100
2-5
102-105
100
2-5
102-105
Reviving Technique:
1. Place the unqualified rubber products and production leftovers on the open mill after selecting, cleaning, removing sundries, drying
and cutting into small pieces, break them with small roll pitch (≤0.2mm), and make them be powder after selection and classification.
2. Refine the rubber powder and the RDS rubber reclaiming agent on the open mill for 15-30 min with roll temperature below 50℃.
Corresponding softener can be added according to the condition, and after mill running and sheeting, the revived rubber can be got.
Storage life: in cool and dry places for 2 years
Package: 25kg/bag
RDSiR Silicone Rubber Reclaiming Agent
waste silicone rubber
RDSiR
Total
Reclaiming Technique:
1. Place the unqualified silicone rubber products and production
leftovers on the open mill after selecting, cleaning, removing
sundries, drying and cutting into small pieces, break them with
small roll pitch (≤0.2mm), and make them be silicone rubber
powder after selection and classification.
2. Refine 20 meshes silicone rubber powder and RDSiR silicone
rubber reclaiming agent on the open mill for 15-20 min with roll
Appearance: light yellow powder
Application:applicable to the reviving of the waste silicone rubber under normal temperature.
Application Recipe:
temperature below 50℃. Corresponding softener can be added
according to the condition, and after mill running and sheeting, the
reclaimed silicone rubber can be got.
3. Notes: The reviving of silicone rubber is apt to mix on the open
mill at low speed ratio; the higher the speed ratio the harder to
sheet; it is recommended to operate on the open mill with the speed
ratio of 1:1.1.
Storage life: in cool and dry places for 2 years
Package: 25kg/bag