2. Índice
1. Use of gold mill tailings in making bricks: a feasibility study (Surendra Roy, Govind R. Adhikari,
Rama N. Gupta(2007)).
2. Nuevas tecnologías para el uso y disposición de relaves mineros aplicado a Codelco, división el
teniente (MT- Matías Castro Arias (2018)).
3. Recycling of copper tailings as an additive in cement mortars (Obinna Onuaguluchi, Özgur Eren
(2012)).
4. Stabilization characteristics of copper mine tailings through itsutilization as a partial substitute for
cement in concrete: preliminary investigations (Sanghamitra Kundu, Aman Aggarwal, Siddharth
Mazumdar, K. Bhargava Dutt(2016)).
5. Sustainable use of mine waste and tailings with suitable admixture as aggregates in concrete
pavements: A review (B.C. Gayanaa and Karra Ram Chandar ).
6. Copper tailings as supplementary cementitious material: activation, leaching and environmental
behaviour (Felipe Andres Vargas Muñoz(2020)).
3. Use of gold mill tailings in making bricks: a feasibility study
• Creación de ladrillos con material de relave proveniente de una mina de oro.
• Material de relave con plasticidad igual a cero.
• Utilización de adhesivos:
• Cemento Portland
• Black cotton soils
• Red Soils
• Se denominaron dos tipos de ladrillos:
• Cement-tailings bricks
• Soils-tailings bricks
• Los ladrillos deben cumplir al menos:
• Resistencia a la compresión > 35 𝐾𝑔 𝑐𝑚2
• Absorción de agua < 20 % (Considerando una exposición de 24 hrs)
• Contracción Lineal +/- 3%
4. Use of gold mill tailings in making bricks: a feasibility study
Para el suelo, se analizo la creación de ladrillos con distintos porcentajes de
material de relave:
5. Use of gold mill tailings in making bricks: a feasibility study
• Cement-tailings bricks:
Los ladrillos de cemento luego de realizarlos,
solo necesitaban pasar por un proceso de
curado, no necesitaban ser “horneados” por
ende la idoneidad de ellos se baso en realizar
ensayos de resistencia a la compresión para
distintos periodos de curado.
En base a lo anterior, los ladrillos con un 20%
de cemento o más, y un proceso de curado de
7 días o más cumplían con los requerimientos.
6. Use of gold mill tailings in making bricks: a feasibility study
• Soil-tailings bricks:
Estos ladrillos debieron pasar por un proceso
de secado, primero a temperatura ambiente,
luego al sol y finalmente en un horno, por
ende se analizaron propiedades como la
resistencia a la compresión, la absorción de
agua y la contracción lineal, a distintas
temperaturas de “cocción”.
7. Use of gold mill tailings in making bricks: a feasibility study
• Soil-tailings bricks:
Estos ladrillos debieron pasar por un proceso
de secado, primero a temperatura ambiente,
luego al sol y finalmente en un horno, por
ende se analizaron propiedades como la
resistencia a la compresión, la absorción de
agua y la contracción lineal, a distintas
temperaturas de “cocción”.
8. Use of gold mill tailings in making bricks: a feasibility study
• Soil-tailings bricks:
Estos ladrillos debieron pasar por un proceso
de secado, primero a temperatura ambiente,
luego al sol y finalmente en un horno, por
ende se analizaron propiedades como la
resistencia a la compresión, la absorción de
agua y la contracción lineal, a distintas
temperaturas de “cocción”.
9. Use of gold mill tailings in making bricks: a feasibility study
• Soil-tailings bricks:
Estos ladrillos debieron pasar por un proceso
de secado, primero a temperatura ambiente,
luego al sol y finalmente en un horno, por
ende se analizaron propiedades como la
resistencia a la compresión, la absorción de
agua y la contracción lineal, a distintas
temperaturas de “cocción”.
10. Nuevas tecnologías para el uso y disposición de relaves mineros
aplicado a Codelco, división el teniente
• Se basa en 3 soluciones, las dos primeras son aplicaciones de nuevas tecnologías para variar
la disposición de los relaves.
• La ultima solución y la mas interesante es el uso del material de relave para la construcción
de adoquines en base a la técnica de geopolimerización, en donde el material de relave
reemplazaría al cemento o a la arcilla.
• La metodología planteada es la siguiente:
• Se reemplaza el cemento con material de relave.
• Se mezcla el relave con una solución alcalina.
• La mezcla se activa formando un geopolímero con propiedades satisfactorias.
• Se procede a juntar la mezcla con áridos .
• Se genera hormigón de elevada calidad, hormigón geopolimérico.
11. Recycling of copper tailings as an additive in cement mortars
• Adición de material de relave como aditivo a mezclas para morteros.
• Cuatro mezclas especificas:
• 0 % de material de relave, mezcla control.
• 5% de material de relave
• 5 % de material de relave pre-humedecido
• 10 % de material de relave
12. Recycling of copper tailings as an additive in cement mortars
• Parámetros analizados:
• Mortar Consistency
• Compressive and flexural strength
• Abrasion and impact resistance
• Rate of water absortion
• Acid resistance
• Chloride penetration
13. Recycling of copper tailings as an additive in cement mortars
• Mortar Consistency
14. Recycling of copper tailings as an additive in cement mortars
• Compressive and flexural strength
15. Recycling of copper tailings as an additive in cement mortars
• Abrasion and impact resistance
16. Recycling of copper tailings as an additive in cement mortars
• Rate of water absortion
Las mayores tasas de absorción de agua de las muestras
mezcladas con residuos de cobre se atribuyeron a las
partículas porosas y gruesas de los de los residuos de cobre y
a su baja reactividad.
17. Recycling of copper tailings as an additive in cement mortars
• Acid resistance and Chloride penetration
“Cuando se uso material de relave seco, se provoco aumento en el yield stress, y reducción en el flujo de las
mezclas, para contrarrestar eso se experimento con relaves pre-humedecidos. En todos los otros parámetros
analizados, las muestras con relaves de cobre fueron superiores a la mezcla control.”
18. Stabilization characteristics of copper mine tailings through its
utilization as a partial substitute for cement in concrete
• Reemplazo parcial del cemento por material de relave
• Sustitución entre 0-50 %
• Razón Agua/Aglutinante = 0.5
• Como agregado grueso se utilizó piedra triturada en proporciones iguales de 20 mm y 10 mm, con una
gravedad específica media de 2,74.
19. Stabilization characteristics of copper mine tailings through its
utilization as a partial substitute for cement in concrete
• La propiedad granular del cemento es fundamental para controlar la velocidad de fraguado y el aumento de
la resistencia del cemento y, por lo tanto, se desea una amplia variedad de tamaños de partícula y formas
angulares para obtener un buen cemento trabajable.
20. Stabilization characteristics of copper mine tailings through its
utilization as a partial substitute for cement in concrete
• Compressive strength
• Pruebas realizadas a los 3, 7 y 28 días de
curado.
• Reducción de la resistencia a la
compresión, para mezclas con material de
relave.
• Sin embargo la mezcla con 10% MT es
similar a la muestra sin MT, y esto puede
convenir en temas de costos.
• Se recomienda probar otras
combinaciones de la relación W/B
21. Sustainable use of mine waste and tailings with suitable
admixture as aggregates in concrete pavements
• Review
• Reemplazo parcial del cemento, dentro del rango de 5-15 % , con relaves de mineral de
hierro, con una disminución considerable de la resistencia a la compresión en los rangos
15-25 % (Ravi Kumar (2012))
• Zhao et al. (2014) Sustitución de la arena por relaves de mineral de hierro para preparar el
UPHC (Ultra High Performance Concrete). Con 40% para muestras de curado estándar de
90 días, la resistencia a la compresión disminuía menos del 11% y la resistencia a la
flexión aumentaba un 8%.
22. Sustainable use of mine waste and tailings with suitable
admixture as aggregates in concrete pavements
• Review
• Reemplazo total de arena de río por relaves de mineral de hierro, la gravedad específica es
2.6, la densidad relativa es 1.27 gm/cm3, el módulo de finura = 1.05 y la tasa de absorción
de agua es del 7%. En general la resistencia a la compresión aumento para todos los
porcentajes, pero el reemplazo del 25 % es el más optimo, con un aumento del 12.9 % en
su resistencia (Ali (2016)).
• Reemplazo de gruesos por esteril de mineral de hierro de Goa y realizó un estudio
experimental. En la mezcla de concreto, el 40% de los agregados gruesos fueron
reemplazados por relaves de mineral de hierro y los bloques de concreto se hicieron
durante 28 días de curado. El resultado fue una resistencia comparativa de 21,93 MPa
frente a la del agregado de granito de 19,91 MPa. Por lo tanto, se notó el aumento en la
resistencia a la compresión con los relaves de mineral de hierro con respecto al
agregado grueso convencional (Yellishetty (2008)).
23. Copper tailings as supplementary cementitious material:
activation, leaching and environmental behaviour
• Uso de material de relave como material cementante suplementario.
• Ensayo de resistencia a la compresión a las mezclas con relave no tratado, 20%, 40% y 50%.
• Todos los ensayos tuvieron menor resistencia que el cemento portland, con respecto a la misma relación
W/C.
• Además dependiendo el material de relave varia la resistencia.
• Pero si en vez de considerar la sustitución se considera como suplemento las resistencias aumentan.
• Ahora si se trata el material de relave, aumentan significativamente sus resistencias.